Types |
Varieties |
NO. |
Index |
Features and Main use |
Appearance |
Solid content
% |
Viscosity
s/T-4,25℃ |
Drying time |
Curing time |
Heat tolerance |
Loss on heat
3h/250℃,% |
Pure organosilicon |
one-pack high temperature dyr type |
Methylphenyl silicone resin |
1053 |
milk-white light alowed, no mechanical impurities, light yellow to reddish brown transparent liquid. |
≥50 |
25-60 |
≤2h/200℃ |
|
＞200h/200℃ |
≤5 |
fire resistant coatings, used for transformer of engines
|
1054 |
≥55 |
25-65 |
≤2h/200℃ |
|
＞200h/200℃ |
＜6 |
fire resistant coatings |
1152 |
≥55 |
25-75 |
≤2h/200℃ |
|
＞200h/200℃ |
≤3 |
glass cloth used for the electric insulation of engines |
1153 |
≥55 |
20-55 |
≤2h/200℃ |
|
＞200h/200℃ |
≤5 |
mica plate, mica tape, capacitor |
methylsilyl resin |
SAR-2 |
30±2.5 |
6-25mpa.s |
20’/70℃ |
|
|
|
glass resin |
SAR-5 |
30±2.5 |
5-15mpa.s |
|
|
|
|
protective caoting of kinescope anode |
SAR-9 |
≥50 |
8-35 |
|
|
|
|
adhesive of fire-resistant mica powder |
one-pack room temperature dry type |
Methylphenyl silicone resin |
WJ-2 |
≥50 |
≥20 |
＜1h/25℃ |
2h/180℃ |
2h/300℃ |
|
room temperature fast drying, high hardness, high adhesive force, good heat resistance |
WJ-2B |
≥50 |
≥20 |
＜2h/25℃ |
2h/180℃ |
2h/300℃ |
|
suitable for large equipments used in high temperature |
WJ-3 |
≥50 |
≥20 |
＜10’/25℃ |
2h/220℃ |
2h/300℃ |
|
room temperature fast drying, high hardness, impact resistant, heat resistant, suitable for large equipments used in high temperature |
2Kroom temperature cross-linking |
WJ-1 |
≥50 |
20-55 |
＜3h/25℃ |
|
300h/200℃
0.5h/300℃ |
|
2K, room temperature curing, room temperature dying, suitable for large equipments used in high temperature |